PLA Marble - Red Granite (s kolutom) 1kg
Bambu Lab
Lastnosti izdelka
· Naravna tekstura podobna kamnu
· Vključuje osnovni kolut za večkratno uporabo
· Premer: 1,75 mm ± 0,03 mm
Opozorila za uporabo
· Združljivo z AMS in AMS lite
· Ni združljivo z 0,2 mm šobo
· Barva: Rdeči granit (13201)
Cena:
23,52 €
28,69 € z DDV
Produkta ni na lokalni zalogi
Specifications
Filament Diameter: 1.75 mm
Net Filament Weight: 1 kg
Spool Material: ABS (Temperature resistance: 70°C)
Spool Diameter: 200 mm
Spool Height: 67 mm
Recommended Printing Settings
Drying Settings before Printing: 55°C, 8 hours
Printing and Storage Humidity: < 20% RH (Sealed with desiccant)
Nozzle Size: 0.4, 0.6, 0.8 mm
Nozzle Temperature: 190 - 230°C
Build Plate Type: Cool Plate, High Temperature Plate, or Textured PEI Plate
Bed Surface Preparation: Glue
Bed Temperature: 35 - 45°C
Cooling Fan: Turn on
Printing Speed: < 250 mm/s
Retraction Length: 0.6 - 1.0 mm
Retraction Speed: 20 - 40 mm/s
Chamber Temperature: 25 - 45°C
Max Overhang Angle: 55°
Max Bridging Length: 30 mm
Support Material: Support for PLA
Physical Properties
Density (ISO 1183): 1.22 g/cm3
Melt Index (210°C, 2.16 kg): 32.2 ± 4.5 g/10 min
Melting Temperature (DSC, 10°C/min): 156°C
Glass Transition Temperature (DSC, 10°C/min): 56°C
Crystallization Temperature (DSC, 10°C/min): N/A
Vicat Softening Temperature (ISO 306, GB/T 1633): 57°C
Heat Deflection Temperature (ISO 75, 1.8 MPa): 53°C
Heat Deflection Temperature (ISO 75, 0.45 MPa): 56°C
Saturated Water Absorption Rate (25°C, 55% RH): 0.44%
Mechanical Properties
Young's Modulus (X-Y, ISO 527, GB/T 1040): 2330 ± 240 MPa
Young's Modulus (Z, ISO 527, GB/T 1040): 1970 ± 210 MPa
Tensile Strength (X-Y, ISO 527, GB/T 1040): 33 ± 4 MPa
Tensile Strength (Z, ISO 527, GB/T 1040): 30 ± 4 MPa
Breaking Elongation Rate (X-Y, ISO 527, GB/T 1040): 6.7 ± 0.5 %
Breaking Elongation Rate (Z, ISO 527, GB/T 1040): 5.3 ± 0.4 %
Bending Modulus (X-Y, ISO 178, GB/T 9341): 2920 ± 180 MPa
Bending Modulus (Z, ISO 178, GB/T 9341): 2560 ± 170 MPa
Bending Strength (X-Y, ISO 178, GB/T 9341): 75 ± 5 MPa
Bending Strength (Z, ISO 178, GB/T 9341): 55 ± 4 MPa
Impact Strength (X-Y, ISO 179, GB/T 1043): 24.0 ± 2.5 kJ/m2; 9.5 ± 2.6 kJ/m2 (notched)
Impact Strength (Z, ISO 179, GB/T 1043): 6.5 ± 0.8 kJ/m2
Other Physical and Chemical Properties
Odor: Odorless PLA
Skin Hazards: No hazard
Chemical Stability: Stable under normal storage and handling conditions
Solubility: Insoluble in water
Resistance to Acid: Not resistant
Resistance to Alkali: Not resistant
Resistance to Organic Solvent: Not resistant
Resistance to Oil and Grease: Resistant to most oils
Flammability: Flammable
Combustion Products: Water, carbon oxides
Odor of Combustion: Odorless
Specimen Test Printing Conditions
Nozzle Temperature: 220°C
Bed Temperature: 35°C
Printing Speed: 200 mm/s
Infill Density: 100%
Filament Diameter: 1.75 mm
Net Filament Weight: 1 kg
Spool Material: ABS (Temperature resistance: 70°C)
Spool Diameter: 200 mm
Spool Height: 67 mm
Recommended Printing Settings
Drying Settings before Printing: 55°C, 8 hours
Printing and Storage Humidity: < 20% RH (Sealed with desiccant)
Nozzle Size: 0.4, 0.6, 0.8 mm
Nozzle Temperature: 190 - 230°C
Build Plate Type: Cool Plate, High Temperature Plate, or Textured PEI Plate
Bed Surface Preparation: Glue
Bed Temperature: 35 - 45°C
Cooling Fan: Turn on
Printing Speed: < 250 mm/s
Retraction Length: 0.6 - 1.0 mm
Retraction Speed: 20 - 40 mm/s
Chamber Temperature: 25 - 45°C
Max Overhang Angle: 55°
Max Bridging Length: 30 mm
Support Material: Support for PLA
Physical Properties
Density (ISO 1183): 1.22 g/cm3
Melt Index (210°C, 2.16 kg): 32.2 ± 4.5 g/10 min
Melting Temperature (DSC, 10°C/min): 156°C
Glass Transition Temperature (DSC, 10°C/min): 56°C
Crystallization Temperature (DSC, 10°C/min): N/A
Vicat Softening Temperature (ISO 306, GB/T 1633): 57°C
Heat Deflection Temperature (ISO 75, 1.8 MPa): 53°C
Heat Deflection Temperature (ISO 75, 0.45 MPa): 56°C
Saturated Water Absorption Rate (25°C, 55% RH): 0.44%
Mechanical Properties
Young's Modulus (X-Y, ISO 527, GB/T 1040): 2330 ± 240 MPa
Young's Modulus (Z, ISO 527, GB/T 1040): 1970 ± 210 MPa
Tensile Strength (X-Y, ISO 527, GB/T 1040): 33 ± 4 MPa
Tensile Strength (Z, ISO 527, GB/T 1040): 30 ± 4 MPa
Breaking Elongation Rate (X-Y, ISO 527, GB/T 1040): 6.7 ± 0.5 %
Breaking Elongation Rate (Z, ISO 527, GB/T 1040): 5.3 ± 0.4 %
Bending Modulus (X-Y, ISO 178, GB/T 9341): 2920 ± 180 MPa
Bending Modulus (Z, ISO 178, GB/T 9341): 2560 ± 170 MPa
Bending Strength (X-Y, ISO 178, GB/T 9341): 75 ± 5 MPa
Bending Strength (Z, ISO 178, GB/T 9341): 55 ± 4 MPa
Impact Strength (X-Y, ISO 179, GB/T 1043): 24.0 ± 2.5 kJ/m2; 9.5 ± 2.6 kJ/m2 (notched)
Impact Strength (Z, ISO 179, GB/T 1043): 6.5 ± 0.8 kJ/m2
Other Physical and Chemical Properties
Odor: Odorless PLA
Skin Hazards: No hazard
Chemical Stability: Stable under normal storage and handling conditions
Solubility: Insoluble in water
Resistance to Acid: Not resistant
Resistance to Alkali: Not resistant
Resistance to Organic Solvent: Not resistant
Resistance to Oil and Grease: Resistant to most oils
Flammability: Flammable
Combustion Products: Water, carbon oxides
Odor of Combustion: Odorless
Specimen Test Printing Conditions
Nozzle Temperature: 220°C
Bed Temperature: 35°C
Printing Speed: 200 mm/s
Infill Density: 100%