PLA Silk Dual Color (with spool) 1kg
Bambu Lab
Bambu PLA Silk Dual-Color filament is crafted from two individual silk colors seamlessly blended into a single strand. Retaining its silky texture and high-gloss features, this filament transitions between two colors, creating a natural and smooth gradient. You can easily change the visible color by rotating the color-blending filament to different orientations. Ideal for printing aesthetic parts and decorative objects. Elevate your creations with the smooth and captivating allure of PLA Silk Dual-Color filament.
Captivating Silk Appearance with Dynamic Color Transformations
Crafted from two individual colors seamlessly merged into a single filament strand, this filament promises a mesmerizing silk appearance. Simply rotate the model to see different color effects, revealing enchanting color fusions that spark your creativity.
Master The Glossy Finish
The gloss finish of the model printed by Silk material can be controlled by printing temperature and speed. To get glossier finish, higher printing temperatures and/or lower speeds are recommended.
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Choose your option:
Price:
From 23,52 €
28,69 € inc. VAT
Stock: Select an option to view stock!
Specifications
Filament Diameter: 1.75 mm
Net Filament Weight: 1 kg
Spool Material: ABS (Temperature resistance: 70°C)
Spool Diameter: 200 mm
Spool Height: 67 mm
Recommended Printing Settings
Drying Settings before Printing: 55°C, 8 hours
Printing and Storage Humidity: < 20% RH (Sealed with desiccant)
Blast Drying Oven: 55°C, 8 hours
X1 Series Printer Heatbed: 65 - 75°C, 12 hours
Nozzle Size: 0.2, 0.4, 0.6, 0.8 mm
Nozzle Temperature: 210 - 240°C
Bed Type: Cool Plate, High Temperature Plate, or Textured PEI Plate
Bed Surface Preparation: Glue
Bed Temperature: 35 - 45°C
Cooling Fan: Turn on
Printing Speed: < 250 mm/s
Retraction Length: 0.6 - 1.0 mm
Retraction Speed: 20 - 40 mm/s
Chamber Temperature: 25 - 45°C
Max Overhang Angle: 55°
Max Bridging Length: ~30 mm
Support Material: Support for PLA
Physical Properties
Density (ISO 1183): 1.32 g/cm3
Melt Index (210°C, 2.16 kg): 20.5 ± 1.2 g/10 min
Melting Temperature (DSC, 10°C/min): 152°C
Glass Transition Temperature (DSC, 10°C/min): 57°C
Crystallization Temperature (DSC, 10°C/min): N/A
Vicat Softening Temperature (ISO 306, GB/T 1633): 56°C
Heat Deflection Temperature (ISO 75, 1.8 MPa): 50°C
Heat Deflection Temperature (ISO 75, 0.45 MPa): 53°C
Saturated Water Absorption Rate (25°C, 55% RH): 0.52%
Mechanical Properties
Young's Modulus (X-Y, ISO 527, GB/T 1040): 1830 ± 210 MPa
Young's Modulus (Z, ISO 527, GB/T 1040): 1250 ± 140 MPa
Tensile Strength (X-Y, ISO 527, GB/T 1040): 27 ± 4 MPa
Tensile Strength (Z, ISO 527, GB/T 1040): 18 ± 4 MPa
Breaking Elongation Rate (X-Y, ISO 527, GB/T 1040): 3.5 ± 0.6 %
Breaking Elongation Rate (Z, ISO 527, GB/T 1040): 1.7 ± 0.2 %
Bending Modulus (X-Y, ISO 178, GB/T 9341): 2370 ± 150 MPa
Bending Modulus (Z, ISO 178, GB/T 9341): 1840 ± 160 MPa
Bending Strength (X-Y, ISO 178, GB/T 9341): 66 ± 4 MPa
Bending Strength (Z, ISO 178, GB/T 9341): 21 ± 5 MPa
Impact Strength (X-Y, ISO 179, GB/T 1043): 24.5 ± 1.7 kJ/m2; 8.2 ± 0.5 kJ/m2 (notched)
Impact Strength (Z, ISO 179, GB/T 1043): 4.6 ± 1.1 kJ/m2
Other Physical and Chemical Properties
Odor: Odorless Polylactic Acid
Skin Hazards: No hazard
Chemical Stability: Stable under normal storage and handling conditions
Solubility: Insoluble in water
Resistance to Acid: Not resistant
Resistance to Alkali: Not resistant
Resistance to Organic Solvent: Not resistant
Resistance to Oil and Grease: Resistant to most oils
Flammability: Flammable
Combustion Products: Water, carbon oxides
Odor of Combustion: Odorless
Specimen Test Printing Conditions
Nozzle Temperature: 230°C
Bed Temperature: 35°C
Printing Speed: 200 mm/s
Infill Density: 100%